1、 Product features

1. Be able to control the ratio of anode to cathode. 2. The anode has good solubility and produces less anode mud. 3. It is convenient to load or supplement anode materials. 4. Anode materials are used to save energy consumption. 5. Characteristics of titanium clad copper: it can not only ensure the original conductivity of copper, but also protect the copper body from corrosion by titanium covering, and greatly reduce the pollution of electroplating and electroplating solution.

2、 Method of use

1. The conductivity of titanium is poor. Generally, the power on current of the hook outside the water is not greater than 0.26a/cm2. Otherwise, the hook body is heated, resulting in an increase in the temperature of the electroplating solution, an increase in the cooling capacity, a waste of electric energy, and even burning the plastic tank due to heating. When it is found that the titanium basket hook is obviously hot, The number of titanium baskets can be increased or the cross-sectional size of titanium basket hook can be increased. The conductivity of titanium basket. 2. Titanium blue hook and electrode generally do not use plane or circular contact, which is easy to cause poor contact and spot corrosion of electrode. 3. The titanium basket opening shall be slightly higher than the liquid level to prevent the outflow of anode slag. 4. The lower end of the titanium basket shall be 100-150mm higher than the parts to avoid the current concentration of the parts at the lower end and scorching. 5. The titanium basket should be in close contact with the anode, otherwise the anode potential on the titanium basket will rise sharply, resulting in oxygen and chlorine evolution reaction on the surface of titanium blue, causing damage to titanium blue and oxidation of additives. 6. In order to prevent burrs on the coating, the anode bag should be wrapped around the titanium basket, because the bag is usually used for a long time without removal, Therefore, it is suggested to use the method of "double-layer bag". 7. The anode bag should wrap the titanium basket mouth tightly, and a few centimeters gap should be reserved at the bottom of the bag to store the possible anode sludge.

3、 Characteristics

The value of the titanium copper composite rod process is that it can closely combine titanium and copper into one in the organizational structure, just like the connection of skin and flesh. This combination will not increase the resistance of current. It can enable copper to give full play to its essentially original conductivity, and can also add the following four advantages on the basis of not affecting the original excellent conductivity of copper:

Support strength:

The yield strength of titanium copper composite rod reaches 135Mpa and the tensile shear strength reaches 180260mpa, which fully meets the production design requirements and achieves the support performance required by the anode during operation.

Corrosion resistance:

The outer layer of the titanium copper composite rod is in direct contact with the electrolytic medium. The pure titanium in the outer layer has excellent and its service life is more than 10 times longer than that of other materials.

Energy saving:

Because the explosion + rolling production process adopted can make titanium and copper completely and closely compound without delamination, greatly reduce the pollution of electrolyte and electroplating solution, and greatly reduce the current resistance to 7.77 × 10-6 Ω, making the current smoother, thus saving energy consumption.

Improve the effect:

Because the production process of explosion + rolling method can make titanium and copper completely and closely compound without liquid pollution caused by delamination, because the corrosion resistance of outer titanium does not produce air and environmental pollution caused by oxidation, and also greatly reduce the overall environmental pollution. We can produce different specifications of titanium clad copper and zirconium clad copper according to user requirements.